S235J0 | 1.0114

Grade S235J0 has a minimum yield strength of 235 MPa. The impact energy at a test temperature of 0°C is at least 27 joules. Steels of grade S235J0 are suitable for low-stressed parts in steel and mechanical engineering with increased toughness and weldability.

S235J0 - send request!

Non-alloy/general structural steel

S235J0 | 1.0114: Properties according to DIN EN 10 025-2

Steel type

Short designation	VDA239-100*	Material number
S235J0	-	1.0114

* Comparative grade, therefore minor deviations from DIN EN values possible

S235J0 | 1.0114: Mechanical properties, transverse 1)

Upper yield strength ReH MPa min.	Tensile strength Rm MPa		Elongation at fracture A80 % min.					Elongation at fracture A 5 % min.
e ≤ 16 mm	e < 3 mm	3 mm ≤ e ≤ 16 mm	e ≤ 1 mm	1 mm < e ≤ 1.5 mm	1.5 mm < e ≤ 2 mm	2 mm < e ≤ 2.5 mm	2.5 mm < e < 3 mm	3 mm ≤ e ≤ 16 mm
235	360-510	360–510	15	16	17	18	19	24

S235J0 | 1.0114: Chemical composition (heat analysis)

Percentage by weight % max.
C	Si	Mn	P	S	N	Cu
0.17	-	1.40	0.030	0.030	0.012	0.55

Your product of choice: S235J0 | 1.0114

Send request!

1) As rolling widths ≥ 600 mm are primarily used, transverse values generally apply, refer to DIN EN 10 025-2.