Martensitic steel | HDT1180G1+ZE

Choose your electrolytically zinc-coated Martensitic steel in the grade HDT1180G1+ZE here.

The experts at our locations are happy to advise you. We look forward to hearing from you.

Multiphase steel ∙ DIN EN 10 338

Martensitic phase steel

Short name	VDA239-100*	Surface finish	Material number	Tensile strength R _p0,2¹⁾MPa	Tensile strength R_mMPa	Elongation at break A₈₀²⁾% min.	Elongation at break A³⁾% min.
HDT1180G1	HR900Y1180T-MS	+ZE	1.0960	900-1.200	1.180	4	5

_{1) XG = dual phase with increased yield strength}

_{2) Reduced minimum values of elongation at break apply to product thicknesses t < 0.60 mm (minus 2 units). * Comparative grade, therefore slight deviations from DIN EN values possible}

_{3) Elongation at break for a proportional sample with L0 = 5.65 √S0 for sheet thicknesses ≥ 3.0 mm}

Short name	VDA239-100*	Surface finish	Material number	Mass % max.
		C	Si	Mn	P	S	AItotal(from/to)	Cr+Mo	Nb+Ti	V	B
HDT1180G1	HR900Y1180T-MS	+ZE	1.0960	0.25	0.80	2.50	0.060	0.015	0.015-2.0	1.20	0.25	0.22	0.005

_{1) XG = dual phase with increased yield strength}

* Comparative grade, therefore slight deviations from DIN EN values possible