EN AW 5005A | Al Mg1(C)
EN AW 5005A is an aluminum alloy with magnesium. On this page you can find the chemical and mechanical specifications of the alloy EN AW 5005A | Al Mg1(C).
Other dimensions and alloys are available on request.
Our aluminum specialists in Mannheim are happy to advise you. EN AW 5005A - send request!
Chemical composition [% max. or range]
| Si | Fe | Cu | Mn | Mg | Cr | Ni | Zn | Ti | Ga | V |
| 0.3 | 0.5 | 0.05 | 0.15 | 0.7–1.1 | 0.1 | — | 0.2 | — | — | — |
EN AW 5005A | Al Mg1(C): Heat-treated condition 0/H111
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 29 | 35 | 100 - 145 | 15 | 0 t | 0 t | |
| 0.5 - 1.5 | 29 | 35 | 100 - 145 | 19 | 0 t | 0 t | |
| 1.5 - 3 | 29 | 35 | 100 - 145 | 20 | 0.5 t | 0 t | |
| 3 - 6 | 29 | 35 | 100 - 145 | 22 | 1.0 t | 1.0 t | |
| 6 - 12.5 | 29 | 35 | 100 - 145 | 24 | 1.5 t | ||
| 12.5 - 50 | 29 | 35 | 100 - 145 | 20 |
EN AW 5005A | Al Mg1(C): Heat-treated condition H14
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 48 | 120 | 145 - 185 | 2 | 2.0 t | 0.5 t | |
| 0.5 - 1.5 | 48 | 120 | 145 - 185 | 2 | 2.0 t | 1.0 t | |
| 1.5 - 3 | 48 | 120 | 145 - 185 | 3 | 2.5 t | 1.0 t | |
| 3 - 6 | 48 | 120 | 145 - 185 | 4 | 2.0 t | ||
| 6 - 12.5 | 48 | 120 | 145 - 185 | 5 | 2.5 t |
EN AW 5005A | Al Mg1(C): Heat-treated condition H22
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 38 | 80 | 125 - 165 | 4 | 1.0 t | 0 t | |
| 0.5 - 1.5 | 38 | 80 | 125 - 165 | 5 | 1.0 t | 0.5 t | |
| 1.5 - 3 | 38 | 80 | 125 - 165 | 6 | 1.5 t | 1.0 t | |
| 3 - 6 | 38 | 80 | 125 - 165 | 8 | 1.0 t | ||
| 6 - 12.5 | 38 | 80 | 125 - 165 | 10 | 2.0 t |
EN AW 5005A | Al Mg1(C): Heat-treated condition H24
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 47 | 110 | 145 - 185 | 3 | 1.5 t | 0.5 t | |
| 0.5 - 1.5 | 47 | 110 | 145 - 185 | 4 | 1.5 t | 1.0 t | |
| 1.5 - 3 | 47 | 110 | 145 - 185 | 5 | 2.0 t | 1.0 t | |
| 3 - 6 | 47 | 110 | 145 - 185 | 6 | 2.0 t | ||
| 6 - 12.5 | 47 | 110 | 145 - 185 | 8 | 2.5 t |
EN AW 5005A | Al Mg1(C): Heat-treated condition H26
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 52 | 135 | 165 - 205 | 2 | 1.0 t | ||
| 0.5 - 1.5 | 52 | 135 | 165 - 205 | 3 | 1.5 t | ||
| 1.5 - 3 | 52 | 135 | 165 - 205 | 4 | 2.0 t | ||
| 3 - 4 | 52 | 135 | 165 - 205 | 4 | 2.5 t |
Heat-treated condition H28 | EN AW 5005A
Mechanical properties
| Nominal thickness mm | Brinell hardness HBW | Yield strength Rp0,2 MPa min./max. | Tensile strength Rm MPa min./max. | Elongation A50 mm % min. | Elongation A % min. | Bending radius 180° t min. | Bending radius 90° t min. |
| 0.2 - 0.5 | 58 | 160 | 185 | 1 | 1.5 t | ||
| 0.5 - 1.5 | 58 | 160 | 185 | 2 | 2.5 t | ||
| 1.5 - 3 | 58 | 160 | 185 | 3 | 3.0 t |